The inhibition effect of the grape pomace extract during the early stage of steel corrosion under adsorbed thin electrolyte layers was investigated. The present study was carried out to identify the components present in the 2-propanol grape pomace extract by GC-MS analysis. Gravimetric, electrochemical impedance spectroscopy, potentiodynamic polarization, scanning electron microscopy, and FTIR techniques were used to study the corrosion inhibitive. Polarization measurements have indicated that these green inhibitors acted through mixed type inhibition. SEM studies have evidenced the formation of a protective film over metal surface while FTIR supported by molecular modelling has proved that this shielding effect was caused by aldehydes particularly 2-phenylacetaldehyde and 3,7-dimethylocta-2,6-dienal.
[1] Zhang D.-Q., Gao L.-X., Zhou G.-D.: Surf. Coat. Technol., 2010, 204, 1646. https://doi.org/10.1016/j.surfcoat.2009.10.054
[2] Zhang D.-Q, An Z.-H., Pan Q.-Y. et al.: Corros. Sci., 2006, 48, 1437. https://doi.org/10.1016/j.corsci.2005.06.007
[3] Quraishi M., Jamal D.: Corrosion, 2002, 58, 5, 387. https://doi.org/10.5006/1.3277627
[4] Bastidas D., Cano E., Mora E.: Anti-Corrosion Methods and Materials, 2005, 52, 71. https://doi.org/10.1108/00035590510584771
[5] Andreatta F. Fedrizzi, L.: Active Protectiv Coatings, 2016, 233, 59. https://doi.org/10.1007/978-94-017-7540-3_4
[6] Taleb H. Ibrahim, Elron E. Gomes, Ime B. Obot et al.: J. Adhes. Sci. Technol., 2017, 31, 2697. https://doi.org/10.1080/01694243.2017.1317458
[7] Raja P., Sethuraman M.: Mat. Lett., 2008, 62, 113. https://doi.org/10.1016/j.matlet.2007.04.079
[8] Abd-El-Nabey B., Abdel-Gaber A., Said Ali M. et al.: Int. J. Electrochem. Sci., 2013, 8, 7124.
[9] Radojcˇic´ I., Berkovic´ K., KovacˇS., et al.: Corros. Sci., 2008, 50, 5 1498. https://doi.org/10.1016/j.corsci.2008.01.013
[10] Poongothai N., Rajendran P., Natesan M. et al.: Indian J. Chem. Technol., 2005, 12, 641.
[11] Premkumar P., Kannan K., Natesan M.: Asian J. Chem., 2008, 20, 445.
[12] Premkumar P., Kannan K., Natesan M.: J. Metall. Mat. Sci., 2008, 50, 227.
[13] Vorob’iova V., Chyhyrynets’ O., Vasyl’kevych O.: Mater. Sci., 2015, 50, 726. https://doi.org/10.1007/s11003-015-9778-z
[14] Chygyrynets’ E., Vorobyova V.: Chem. Chem. Technol., 2014, 8, 235.
[15] Chyhyrynets O., Vorob'iova V.: Mater. Sci., 2013, 49, 318. https://doi.org/10.1007/s11003-013-9617-z
[16] Leygraf C., Wallinder I., Tidblad J., Graedel T.: Atmospheric Corrosion, John Wiley & Sons, Inc., Hoboken 2016.
[17] Kaya S., Tüzün B., Kaya C., Obot I.: J. Taiwan Inst. Chem. Eng., 2016, 58, 528. https://doi.org/10.1016/j.jtice.2015.06.009
[18] Gece G.: Corros. Science, 2008, 50, 2981. https://doi.org/10.1016/j.corsci.2008.08.043
[19] Koopmans T.: Physica, 1934, 1, 104. https://doi.org/10.1016/S0031-8914(34)90011-2
[20] Kovacevic N., Kokalj A.: Corrosion Science 2011, 53, 909. https://doi.org/10.1016/j.corsci.2010.11.016
[21] Parr R., Pearson R.: J. Am. Chem. Soc., 1983, 105, 7512. https://doi.org/10.1021/ja00364a005
[22] Parr R., Donnelly R., Lewy M., Palke W.: J. Chem. Phys., 1978, 68, 3801. https://doi.org/10.1063/1.436185
[23] Pearson R.: Proc. Natl. Acad. Sci. USA, 1986, 83, 8440. https://doi.org/10.1073/pnas.83.22.8440
[24] Chattaraj P., Sarkar R., Roy D.: Chem. Rev., 2006, 106, 2065. https://doi.org/10.1021/cr040109f
[25] Parr R., von Szentpaly L., Liu S.: J. Am. Chem. Soc., 1999, 121, 1922. https://doi.org/10.1021/ja983494x
[26] Kaya S., Kaya C.: Comput. Theor. Chem., 2015, 1052, 42. https://doi.org/10.1016/j.comptc.2014.11.017
[27] HyperChemTM, Hypercube, Inc., Ontario, Canada 1994.
[28] Lukovits I., Kálmán E., Zucchi F.: Corrosion. 2001, 57, 3. https://doi.org/10.5006/1.3290328