surface morphology

The influence of cavitation on the phase-disperse state of hydrated calcium oxide

The effect of cavitation phenomena excited by ultrasonic radiation and in a jet-type hydrodynamic cavitator on the change in the phase-dispersed state of hydrated calcium oxide was investigated. The influence of the conditions of cavitation activation of calcium hydroxide on the sedimentation stability of its suspension was established. Based on the analysis of the intensity of sedimentation of Ca(OH)2 particles after cavitation treatment of calcium hydroxide suspension, the probable course of this process in different time periods is proposed.

Chemical Leaching of Al3Ni and Al3Ti Alloys at Room Temperature

Al3Ni and Al3Ti alloys were prepared by arc melting and exposed to chemical leaching in 5M NaOH at room temperature. In case of Al3Ni alloy, Al reached phases react with the leaching solution to produce nanoporous nickel with a pore diameter in the range of ~10–20 nm. Only pure Al phase of Al3Ti alloy chemically reacts with the production of a dense wrinkled surface with a wrinkle size of ~50–100 nm.

Гідрохімічний синтез тонких плівок цинку селеніду (znse) в присутності натрію гідроксиду та їхні властивості

Тонкі плівки цинку селеніду (ZnSe) синтезовано з водного розчину натрію
гідроксиду на скляних підкладках. Методом інверсійної вольтамперометрії встановлено
вплив концентрації вихідної цинк-вмісної солі, комплексуючого реагенту натрію
гідроксиду, іонів Селену та гідразину гідрату на масу Цинку в плівках ZnSe за різної
тривалості і температури осадження. На основі отриманих даних оптимізовано умови
синтезу тонких плівок цинку селеніду. Досліджено структуру, оптичні властивості,