ceramics

The sintering regularities of the developed majolica masses compositions on the basis of typicalmass MKL-1 and MK-4K with the addition of broken glass and ceramic bricks wereinvestigated. Theinfluence of these sintering processes additives of the studied mass compositions depending on theircontent and firing temperature is established. A new method of decorating ceramics at the stage of its plastic state was developed. The obtained results will be used to improve the technological processesof obtaining decorative and applied ceramics.

The work describes a method of modifying the ceramic materials by introducing carbon-based nanoscopic additives into the slip composite and glaze composite in the form of water-based suspension for the production of sanitary and technical ceramics of increased quality. Physical and mechanical properties of experimental samples are researched. The results of experimental research are obtained in the form of experimentally determined properties of composite materials which were nanomodified by carbon nanostructures.

The experimental researches of regulation of rheology properties of clay mixture by using to clays the additives of mineral and organiccontained electrolytes in ceramics technology are given.  Подано експериментальні дослідження регулювання реологічних властивостей шлікерів за допомогою використання до глин добавок мінеральних і органовмісних електролітів у технології кераміки.

In this article properties of raw material mixtures for making of wall wares, which contain wastes of enriching of coal, clay and hard additions – manganese ore and limestone were investigated. Also, high-quality indexes of wares and degree of fastening of Sul'furu during termoobroblennya, which was conducted in production terms for the temperatures of 950 °С were examined. Досліджено властивості сировинних сумішей для виготовлення стінних виробів, які містять відходи збагачення вугілля, глину і тверді додатки – марганцеву руду та вапняк.

Thermal processes that take place during the burning of raw mixtures at temperatures 9500С. Raw mix for making wall products contain wastes enrichment, chalk and manganese concentrate. Comparison of data obtained with theoretical information.
   Досліджено термічні процеси, які проходять під час випалювання сировинних сумішей за температури 9500С.  Сировинні суміші для виготовлення стінних виробів містять відходи збагачення вугілля, крейду і марганцевий концентрат.   Проведено співставлення одержаних даних із теоретичними відомостями.

Zinc oxide has numerous commercial device applications. Polycrystalline ZnO varistors, for example, are widely used in high voltage and power-related applications in industries such as microelectronics. One of the ways to control the properties of ZnO is its annealing in various environments, including oxygen, which leads to increased hardness and fracture toughness of ceramics.

Вивчали сировинні суміші для виготовлення стінних виробів, які містять відходи збагачення вугілля, крейду і мангановий концентрат. Досліджено вплив лінійної швидкості газів та питомої витрати кисню на хімічні перетворення сполук Сульфуру та Карбону вугілля, які проходять під час випалювання сировинних сумішей за температури 9500С. Досягнуто ступеня зв’язування Сульфуру, достатнього для випуску виробів без доочищення викидних пічних газів. Режим підйому температури збігається з кривою випалювання стінних виробів на виробництві.