The silver nanostructures obtaining was investigated by electrochemical deposition from aqueous solutions (1–10) mM AgNO3 + 50 mМ NaPA) onto graphite substrate. The influence of the concentration of silver ions and cathode potential values in the range E = -0,2 – -1,0 V on surface filling degree and geometry of silver particles was (had been) studied.
A novel conductive ink, suitable for employment in a pressure-sensitive automatic system, was prepared and characterized via scanning electron microscopy, FTIR and differential scanning calorimetry. The ink was obtained as a composite by mixing a solution of ethyl acrylate-methyl acrylate (50/50 ratio) copolymer and carbon black and graphite into a solvent standard for acrylic polymers. The ink average electrical resistance ranges from 40 ohms/cm to 150 ohms/cm.
Exploration studies in Uzbekistan revealed one graphite deposit (Taskazgan) and about 25 sites with varying perspective degree. In order to obtain the graphite for refractory industry uses insufficiently known Rupat, Zauchak and Zahchahona sites were studied. According to the research, Zahchahona site can be classified as a medium-sized field; the refined graphite content in the ore deposit is 3 to 15 %, which meets the requirements of the industry for this type of raw material. Graphite was refined by flotation and leaching process, brought to grade of 75 % carbon.