Nanostructural Characteristics of Polymer Adsorption Layers Formed under Ultrasonic Treatment on Metal Oxides Surface in Aqueous Dispersions

Автори: 
Nikolay Bulychev, Edward Kisterev, Yulia Ioni, Klaus Dirnberger, Vitali Zubov and Claus Eisenbach

The course and the result of the surface modification of titanium dioxide and ferrous oxide pigments in aqueous dispersion by ethylhydroxyethylcellulose (EHEC) without and with mechanical treatment of the dispersion by ultrasonic power was studied by the electrokinetic sonic amplitude (ESA) method. The evaluation of the ESA data showed that the ultrasonic treatment causes a significant thickness increase of the EHEC layer on the pigment which is primarily attributed to the ultrasonically induced activation of the pigment surface. The thickness of the polymer adsorption layer derived from ESA measurements was confirmed by TEM investigations. The ultrasonic treatment leads to significant changes of the adsorption layers properties and is a promising method for the surface modification of pigments with regard to dispersion stability.

[1] Holmberg K., Jönsson B., Kronberg B. and Lindman B.: Surfactants and Polymers in Aqueous Solution”, 2nd edn. J. Wiley & Sons, Chichester, UK 2003.
[2] Netz R. and Andelman D.: Physics Reports, 2003, 380, 1.
[3] Somasundaran P. and Krishnakumar S.: Colloids and Surfaces A,1997, 123, 491.
[4] Theo G. and de Ven V.: Adv. Colloid Interface Sci., 1994, 48, 121.
[5] Somasundaran P. and Yu X.: Adv. Colloid Interface Sci., 1994, 53, 33.
[6] Zubov V., Kuzkina I., Ivankova I and Schmitz O.: Eur. Coating J., 1998, 12, 954.
[7] Zubov V., Kuzkina I., Ivankova I. and Schmitz O.: Eur. Coating J., 1998, 11, 856.
[8] Antonietti M. and Weissenberger M.: Macromol. Rapid. Com., 1997, 18, 295.
[9] Zubov V., Serebryakova N., Arutyunov I. et al.: Colloid J., 2004, 66, 302.
[10] Bulychev N., Arutunov I., Zubov V. et al.: Macromol. Chem. & Phys., 2004, 205, 2457. 
[11] Bulychev N., Fomin V., Arutunov I. et al.: Materialovedenie, 2005, 4, 20.
[12] Eisenbach C., Schaller Ch., Schauer T. and Dirnberger K.: ACS Symposium Series 881 “Particle Sizing and Characterization“, American Chemical Society, 2004, 215. 
[13] Schaller C., Schoger A., Dirnberger K. et al.: Macromol. Symp., 2002, 179, 173.
[14] Schaller C., Schauer T., Dirnberger K. and Eisenbach C.: Eur. Phys. J., 2001, E 6, 365.
[15] O’Brien R.: J. Fluid Mech., 1988, 190, 71.
[16] Carasso M., RowlandsW. and O’Brien R.: J. Colloid Interface Sci., 1997, 193, 200.