Mathematical modeling of 2-hydroxyethylmethacrylate with polyvinylpyrrolidone copolymerization process according to technological parameters of the exothermic reaction has been carried out by Scheffe’s simplex-lattice planning method.  Optimization of polymer monomer composition formula has been carried out and the regression equations of the main parameters of exothermic polymerization –– gelation time, the duration of the gel effect area, and the maximum temperature of the exotherm have been obtained.  Using the mathematical model obtained, the content of the initial composition has been

The development of technology for production of metal-filled hydrogels based on copolymers of 2-hydroxyethyl methacrylate (HEMA) with polyvinylpyrrolidone (PVP) by polymerization with simultaneous chemical reduction of metal ions suggests the grounding and determination of optimal technological parameters for its realization. The diverse influence of the initial polymer-monomer composition (PMС) formula on the main parameters of the exotherm of the copolymerization of HEMA with PVP, which constitute the technological mode of chemical deposition of metals, was experimentally proved.

Composite hydrogel metal-filled materials in many cases during the operation are used in the form of films, in medicine these are membrane different kind, of transdermal drugs, implants, elements of medical equipment intended for installation of a reliable contact with the human body, the instrument making-elements of different sensors (humidity, temperature, pressure, concentration of gaseous and liquid products), etc.

Методами сканувальної електронної мікроскопії, седиментаційного та рентгено-
структурного аналізу досліджено структурні характеристики порошків нікелю,
отриманих хімічним осадженням з водних розчинів. Доведено можливість одержання
порошку металу одночасно з формуванням полімерної матриці на основі кополімерів
полівінілпіролідону з 2-гідроксіетилметакрилатом. Експериментально встановлено
можливість регулювання в широких межах гранулометричного складу та структури
нікелевого наповнювача і, відповідно, властивостей композиційних полімерних мате-