The formation of the hydrogel polymer matrix duringthe gelatin cross-linking with dioxirane derivatives of polyoxyethylene glycolswere studied.The optimal conditions for their synthesis were determined. The characteristics of the hydrogel (swelling in different media, mechanical properties at different temperatures) were obtained depending on the type of dioxirane derivative and prepolymer ratio. The possibility of introducing several drugs into hydrogels was established and the release of these drugs was found to be prolonged.

The paper represents the results of the investigation of the formation of a polymeric matrix of hydrogel due to the structuring of polyacrylamide using its reactive polymeric derivative – poly-N-(hydroxymethyl) acrylamide. Research determined zones of optimum conditions of synthesis and characterized hydrogel depending on pH of media, the ratio between the concentration of prepolymers, and time of synthesis.

Синтезовано просторово зшиті полімерні гідрогелі на основі гідрофільних
кополімерів акриламіду з акриловою кислотою або диметиламіноетилметакрилатом.
Досліджено вплив складу мономерної суміші на кінетику кополімеризації, а також
залежність фізико-хімічних та фізико-механічних властивостей гідрогелів від природи
кополімеру та ступеня структурування. Показано, що отримані гідрогелі є високо-
еластичними, пружними матеріалами, а за швидкістю і ступенем набрякання можуть